| Numéro |
J. Phys. Colloques
Volume 48, Numéro C8, Décembre 1987
Fifth European Conference on Internal Friction and Ultrasonic Attenuation in Solids
|
|
|---|---|---|
| Page(s) | C8-161 - C8-166 | |
| DOI | https://doi.org/10.1051/jphyscol:1987821 | |
Fifth European Conference on Internal Friction and Ultrasonic Attenuation in Solids
J. Phys. Colloques 48 (1987) C8-161-C8-166
DOI: 10.1051/jphyscol:1987821
1 Dpto de Física del Estado Sólido, Facultad de Ciencias, Universidad del Pais Vasco, Aptdo 644, SP-48009 Bilbao, Spain
2 GEMPPM-LA 341, INSA, Bât. 502, F-69621 Villeurbanne Cedex, France
J. Phys. Colloques 48 (1987) C8-161-C8-166
DOI: 10.1051/jphyscol:1987821
INTERNAL FRICTION AT MEDIUM TEMPERATURES IN HIGH PURITY ALUMINIUM
M. L. NÓ1, C. ESNOUF2, G. THOLLET2, J. SAN JUAN1 et G. FANTOZZI21 Dpto de Física del Estado Sólido, Facultad de Ciencias, Universidad del Pais Vasco, Aptdo 644, SP-48009 Bilbao, Spain
2 GEMPPM-LA 341, INSA, Bât. 502, F-69621 Villeurbanne Cedex, France
Résumé
Afin de déterminer le mécanisme qui est à l'origine des
relaxations P1 et P'1 nous avons comparé les résultats
expérimentaux de frottement intérieur et de microscopie électronique d'un Al
99. 9999 %, obtenus autour de 0.5Tf, avec les prévisions théoriques
des différents modèles proposés dans la littérature.
Abstract
In order to determine which mechanism is at the origin of
the P1 and P'1 relaxations, the internal friction and
electron microscopy experimental results of 99.9999 % Al around
0.5Tm have been compared to the theoretical forecasts of different
proposed models.