| Numéro |
J. Phys. Colloques
Volume 47, Numéro C1, Février 1986
Thirteenth International Conference on Science of Ceramics
|
|
|---|---|---|
| Page(s) | C1-31 - C1-35 | |
| DOI | https://doi.org/10.1051/jphyscol:1986105 | |
Thirteenth International Conference on Science of Ceramics
J. Phys. Colloques 47 (1986) C1-31-C1-35
DOI: 10.1051/jphyscol:1986105
1 "Boris Kidrich" Institute for Nuclear Science, P.O.B. 522, Beograd, Yugoslavia
2 Faculty of Technology and Metallurgy, Karnegijeva 4, 11000 Beograd, Yugoslavia
J. Phys. Colloques 47 (1986) C1-31-C1-35
DOI: 10.1051/jphyscol:1986105
FORMATION AND SINTERING OF γ-Al2 O3 WITH MgO ADDITIONS FROM COPRECIPITATED HYDRATES
J. KATANIC-POPOVIC1, M. GASIC1 et Lj. KOSTIC-GVOZDENOVIC21 "Boris Kidrich" Institute for Nuclear Science, P.O.B. 522, Beograd, Yugoslavia
2 Faculty of Technology and Metallurgy, Karnegijeva 4, 11000 Beograd, Yugoslavia
Résumé
Des poudres d'alumine-γ avec un dopage homogène ont été obtenues par calcination des coprécipités A100H - Mg(OH)2 formant des solutions solides. L'influence du dopage, pour des rapports Mg/Al de 0.02 à 0.06 sur le frittage a été analysée par mesure de la densité, de la porosité, des retraits linéaires ainsi que par détermination de la résistance à la traction.
Abstract
The gamma Al2O3 powders with homogeneous doppant distribution were obtained by calcination of coprecipitates consisted of A100H solid solutions with Mg(OH)2. The effect of additive with Mg/Al ion ratio 0.02-0.06 on sintering was analysed by density, porosity, linear shrinkage and tensile strength determinations.