| Numéro |
J. Phys. Colloques
Volume 47, Numéro C1, Février 1986
Thirteenth International Conference on Science of Ceramics
|
|
|---|---|---|
| Page(s) | C1-473 - C1-477 | |
| DOI | https://doi.org/10.1051/jphyscol:1986171 | |
Thirteenth International Conference on Science of Ceramics
J. Phys. Colloques 47 (1986) C1-473-C1-477
DOI: 10.1051/jphyscol:1986171
Laboratory for Advanced Ceramics, Research Laboratory of Engineering Materials, and Department of Materials Science, Tokyo Institute of Technology, 4259, Nagatsuta, Midori, Yokohama 227, Japan
J. Phys. Colloques 47 (1986) C1-473-C1-477
DOI: 10.1051/jphyscol:1986171
RAPID QUENCHING OF MELTS IN THE SYSTEM ZrO2-SiO2-Al2O3
M. YOSHIMURA, M. KANEKO et S. SOMIYALaboratory for Advanced Ceramics, Research Laboratory of Engineering Materials, and Department of Materials Science, Tokyo Institute of Technology, 4259, Nagatsuta, Midori, Yokohama 227, Japan
Résumé
Le domaine de formation de phase amorphe dans le système ZrO2-SiO2- Al2O3 a été déterminé par trempe rapide de mélanges fondus en utilisant un four à arc et un système à rouleaux. Le recuit de la phase amorphe au-dessus de 970 °C conduit à une cristallisation principalement de ZrO2 tétragonale, avec des grains de ≈ 10 nm, et/ou de mullite, avec des grains de 2 à 5 µm.
Abstract
The formation region of amorphous phases has been determined by the rapid quenching of melts in the system ZrO2-SiO2-Al2O3 using arc-imaging furnaces and twin-rollers. Re-heating of the amorphous phase brought about the crystallization mainly of t-ZrO2, ≈10 nm in size, and/or mullite, upto 2 ~ 5 µm in size above 970°C.