| Numéro |
J. Phys. Colloques
Volume 46, Numéro C10, Décembre 1985
Eighth International Conference on Internal Friction and Ultrasonic Attenuation in Solids
|
|
|---|---|---|
| Page(s) | C10-187 - C10-190 | |
| DOI | https://doi.org/10.1051/jphyscol:19851043 | |
Eighth International Conference on Internal Friction and Ultrasonic Attenuation in Solids
J. Phys. Colloques 46 (1985) C10-187-C10-190
DOI: 10.1051/jphyscol:19851043
1 Department of Materials Science, University of Tokyo, Tokyo 113, Japan
2 Faculty of Science and Technology, Meijo University, Nagoya 468, Japan
J. Phys. Colloques 46 (1985) C10-187-C10-190
DOI: 10.1051/jphyscol:19851043
STRAIN AMPLITUDE DEPENDENT DAMPING IN ZINC SINGLE CRYSTALS
N. IGATA1 and T.YOKOYAMA21 Department of Materials Science, University of Tokyo, Tokyo 113, Japan
2 Faculty of Science and Technology, Meijo University, Nagoya 468, Japan
Résumé
L'amortissement en fonction de l'amplitude de contrainte est étudié à l'aide des vibrations en flexion dans une gamme de température entre 100 et 300 K. L'effect hysterésique est observé aux températures plus hautes que 270 k, mais non pas à celles plus basses que 170 k. On peut considérer que ce phénomène est entraîné par la mise en désordre de la polygonisation par l'amplitude de contrainte.
Abstract
The strain-amplitude-dependent damping is studied by flexural vibrations in a temperature range between 100 and 300 K. The hysteresis effect is observed at temperatures above 270 K, but not below 170 K. This phenomenon is considered to be caused by the disorder of polygonization due to stress amplitude.