AMORPHIZATION AND RELATED EFFECTS IN Ni/Ti MULTILAYERS STUDIED BY DIFFERENTIAL SCANNING CALORIMETRY

Abstract
Ni/Ti multilayers of three different gross compositions, all having a composition modulation wavelength of approximately 20 nm, were studied by Differential Scanning Calorimetry. In order to associate the observed heat effects with phase transitions, duplicate samples were heated to selected temperatures and analyzed by X-ray diffraction. It is found that amorphization and dissolution of Ti in Ni occurs in overlapping temperature ranges. Both processes have different activation energies, as is revealed by a novel kinetic analysis. Crystallization of the amorphous phase is observed between 650 K and 750 K. In two of the three specimens (Ni₄₅Ti₅₅ and Ni₇₁Ti₂₉) large endothermal effects are found.

Résumé
Multicouches de Ni/Ti avec trois compositions différentes, toutes avec la même longueur d'onde de composition, ont été étudiées avec Differential Scanning Calorimetry. Pour associer les effets de chaleur avec des transformations de phase, des spécimens doubles ont été réchauffés jusqu'aux températures sélectionnées et analysées avec diffraction des rayons x. Nous avons trouvé, que l'amorphisation et la dissolution de Ti dans Ni ont lieu dans des intervalles de temperature coincidant partiellement. Les deux procéssus ont des énergies d'activation différentes, révelées par une analyse cinétique nouvelle. La cristallisation de la phase amorphe à été observée entre 650 K et 750 K. Dans deux spécimens (Ni₄₅Ti₅₅ and Ni₇₁Ti₂₉) on a trouvé des grands effets endothermes.