CRITICAL STRESS-INDUCED RELAXATION IN RELATION TO LONG-RANGE ORDERING, IN Au3Cu, AND SELF-INDUCED ORDERING, IN AuNi SOLID SOLUTIONS
G. RENAUD1, M. BELAKHOVSKY1, J. HILLAIRET1, M. WUTTIG2, G. BESSENAY3 et S. LEFEBVRE31 CEN de Grenoble, Département de Recherche Fondamentale, Service de Physique, BP 85 X, F-38041 Grenoble Cedex, France
2 University of Maryland, College Park, MD 20742, USA
3 Centre d'Etudes de Chimie Métallurgique, 15, rue G. Urbain, F-94400 Vitry-sur-Seine, France
Abstract
This paper reports the results of combined measurements of
the resistivity and anelasticity of Au3Cu and
Au70Ni30 alloys. The data show anomalies above the
critical temperature for long range order in Au3Cu and below the
spinodal in Au70Ni30. In both cases the anomalies suggest
the existence of intermediate states. In Au3Cu this is a state of
pronounced short range order whereas in Au70Ni30 it is an
intermediately decomposed state.
Résumé
On présente les résultats de mesures combinées de
résistivité et d'anélasticité dans des alliages Au3Cu et
Au70Ni30. Les grandeurs mesurées manifestent des
anomalies, au-dessus de la température critique pour l'ordre à longue distance
dans Au3Cu et au-dessous de la spinodale dans
Au70Ni30. Dans les deux cas, ces anomalies suggèrent
l'existence d'états intermédiaires. Dans Au3Cu, c'est un état
d'ordre à courte distance prononcé, tandis que dans
Au70Ni30, il s'agit d'une forme intermédiaire de
décomposition.