| Numéro |
J. Phys. Colloques
Volume 43, Numéro C9, Décembre 1982
Physics of Non Crystalline SolidsProceedings of the 5th International Conference / Physique des Solides Non Cristallins Comptes rendus du 5ème Congrès International |
|
|---|---|---|
| Page(s) | C9-439 - C9-442 | |
| DOI | https://doi.org/10.1051/jphyscol:1982986 | |
Physics of Non Crystalline Solids
Proceedings of the 5th International Conference / Physique des Solides Non Cristallins
Comptes rendus du 5ème Congrès International
J. Phys. Colloques 43 (1982) C9-439-C9-442
DOI: 10.1051/jphyscol:1982986
Departement of Physics, the Catholic University of America, Washington D.C. 20064, U.S.A.
Proceedings of the 5th International Conference / Physique des Solides Non Cristallins
Comptes rendus du 5ème Congrès International
J. Phys. Colloques 43 (1982) C9-439-C9-442
DOI: 10.1051/jphyscol:1982986
VISCOUS FAILURE OF GLASS AT HIGH SHEAR RATES
J.H. Simmons, R.K. Mohr et C.J. MontroseDepartement of Physics, the Catholic University of America, Washington D.C. 20064, U.S.A.
Résumé
La viscosité d'un verre silico-sodo-calcique a été mesurée pour des vitesses de cisaillement élevées ; un comportement "pseudo-élastique" a été observé. L'analyse des résultats montré que l'augmentation de la vitesse d'écoulement résulte d'un réarrangement structural. Une contrainte de rupture caractéristique est découverte, elle correspond au passage du comportement ductile au fragile.
Abstract
The viscosity of a soda-lime-silica glass was measured at high shear rates and "pseudo-plastic" behavior was observed. An analysis of the data shows that the increased flow results from structural rearrangements in the glass. A characteristic failure stress is discovered and is related to a transition from ductile to brittle behavior.