| Numéro |
J. Phys. Colloques
Volume 41, Numéro C6, Juillet 1980
THIRD EUROPHYSICS TOPICAL CONFERENCELATTICE DEFECTS IN IONIC CRYSTALS |
|
|---|---|---|
| Page(s) | C6-501 - C6-503 | |
| DOI | https://doi.org/10.1051/jphyscol:19806130 | |
THIRD EUROPHYSICS TOPICAL CONFERENCE
LATTICE DEFECTS IN IONIC CRYSTALS
J. Phys. Colloques 41 (1980) C6-501-C6-503
DOI: 10.1051/jphyscol:19806130
COLOUR CENTRES IN OXIDES
W. C. Mallard, F. H. Hsu et E. R. Vance
Department of Physics, Georgia State University, Atlanta, Georgia 30303, U.S.A.
LATTICE DEFECTS IN IONIC CRYSTALS
J. Phys. Colloques 41 (1980) C6-501-C6-503
DOI: 10.1051/jphyscol:19806130
COLOUR CENTRES IN OXIDES
Effect of the V- ↔ V= transformation on positron annihilation lifetime spectra in MgO
W. C. Mallard, F. H. Hsu et E. R. Vance Department of Physics, Georgia State University, Atlanta, Georgia 30303, U.S.A.
Résumé
Les spectres perpétuels de l'annihilation du positron ont été mesurés en MgO : OD-, qui contient ~ 20 ppm des lacunes des cations isolés, qui sont produites par l'irradiation de l'électron. Pour la transformation : V- ↔ V=, les intensités des composants perpétuels les plus dures étaient enchéries un peu dans les lacunes ont attrapé les trous et ont réduit quand les trous étaient relâchés.
Abstract
Positron annihilation lifetime spectra have been measured in MgO : OD- containing ~ 20 ppm of isolated cation vacancies produced by electron irradiation. For the V- ↔ V= transformation, the intensities of the longer-lived lifetime components were enhanced slightly when the vacancies trapped holes and reduced when holes were released.