INTERNAL FRICTION IN RHENIUM

M. RAADSCHELDERS1, 2 and R. DE BATIST1, 3

1  Solid State Physics Department, S. C. K./C. E. N., B-2400 MOL, Belgium
2  Rijksuniversiteit Gent, Belgium. Based on a thesis submitted in partial fulfilment of the requirements for the degree of licentiate in physics at the Rijksuniversiteit Gent.
3  Rijksuniversitair Centrum Antwerpen, Belgium.


Résumé
Le frottement intérieur du rhénium a été mesuré entre 100 et 350 °K à une fréquence d'environ 300 Hz. Les échantillons écrouis présentent un pic à 275 °K et un deuxième, moins prononcé, vers 230 °K. Si ce pic est attribué à la relaxation des dislocations, la valeur de l'enthalpie d'activation est alors estimée à 0,6 eV. Quelques résultats concernant des effets de traitements thermiques ou d'irradiation aux électrons de 12 MeV à température ambiante sont également présentés ; à 100 °C des effets de restauration sont observés.


Abstract
Preliminary results of internal friction measurements in rhenium between 100 and 350 °K are reported. For a frequency of about 300 Hz, an internal friction peak is observed in cold-rolled specimens at about 275 °K, together with a shoulder near 230 °K. Assuming that this peak is due to dislocation relaxation, an activation enthalpy of approximately 0.6 eV is estimated. Some results due to thermal treatment and/or irradiation near room temperature with 12 MeV electrons are also discussed ; it is shown that recovery occurs at 100 °C.


Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.

Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.

Initial download of the metrics may take a while.