| Numéro |
J. Phys. Colloques
Volume 49, Numéro C5, Octobre 1988
Interface Science and Engineering '87An International Conference on the Structure and Properties of Internal Interfaces |
|
|---|---|---|
| Page(s) | C5-299 - C5-304 | |
| DOI | https://doi.org/10.1051/jphyscol:1988536 | |
Interface Science and Engineering '87
An International Conference on the Structure and Properties of Internal Interfaces
J. Phys. Colloques 49 (1988) C5-299-C5-304
DOI: 10.1051/jphyscol:1988536
1 ETCA, 16bis, Av. Prieur-de-la-Côte-d'Or, F-94414 Arcueil Cedex, France
2 CNRS-UA 302, CECM, 15, rue Georges Urbain, F-94499 Vitry, France
An International Conference on the Structure and Properties of Internal Interfaces
J. Phys. Colloques 49 (1988) C5-299-C5-304
DOI: 10.1051/jphyscol:1988536
TEM STUDY OF ZrO2/Al INTERFACE
G. TREMOUILLES1 et R. PORTIER21 ETCA, 16bis, Av. Prieur-de-la-Côte-d'Or, F-94414 Arcueil Cedex, France
2 CNRS-UA 302, CECM, 15, rue Georges Urbain, F-94499 Vitry, France
Résumé
La zircone partiellement stabilisée à l'oxyde d'Yttrium est couplée à de l'Aluminium pur monocristallin par un processus de thermocompression. Une bonne adhésion est obtenue ; des microcristaux d'Alumine sont observés à l'interface. Une diffusion d'Oxygène de la Zircone vers l'Aluminium a permis cette croissance. Des relations d'orientations préférentielles sont observées à l'interface.
Abstract
Yttria partially stabilized Zirconia is coupled to monocrystalline pure Aluminium by thermal-compressive process. A good adhesion is obtained, and Alumina microcrystals are observed at the interface. The Oxygen diffusion from Zirconia allows Alumina's growth. Preferential orientations relationships exist at this interface.