| Numéro |
J. Phys. Colloques
Volume 47, Numéro C1, Février 1986
Thirteenth International Conference on Science of Ceramics
|
|
|---|---|---|
| Page(s) | C1-423 - C1-427 | |
| DOI | https://doi.org/10.1051/jphyscol:1986163 | |
Thirteenth International Conference on Science of Ceramics
J. Phys. Colloques 47 (1986) C1-423-C1-427
DOI: 10.1051/jphyscol:1986163
1 On leave from the Instituto de Cerámica y Vidrio, CSIC, Arganda del Rey, Madrid, España.
2 Dept. Material Science and Min. Eng. and National Center for Electron Microscopy, University of California, Berkeley, CA 94720, U.S.A.
3 Instituto de Cerámica y Vidrio, C.S.I.C., Arganda del Rey, Madrid, Spain
J. Phys. Colloques 47 (1986) C1-423-C1-427
DOI: 10.1051/jphyscol:1986163
REACTION SINTERED ZIRCONIA - MULLITE COMPOSITES WITH CaO
J. RINCON1, G. THOMAS2, P. PENA3, S. DE AZA3 et J. S. MOYA31 On leave from the Instituto de Cerámica y Vidrio, CSIC, Arganda del Rey, Madrid, España.
2 Dept. Material Science and Min. Eng. and National Center for Electron Microscopy, University of California, Berkeley, CA 94720, U.S.A.
3 Instituto de Cerámica y Vidrio, C.S.I.C., Arganda del Rey, Madrid, Spain
Résumé
On a étudié par diffraction de rayons-X, microscopie électronique et microanalyse, le développement de la microstructure et des phases qui conduisent, par frittage réactif avec de la chaux, à un composé final dense de zircone-mullite.
Abstract
The development of microstructure and phases leading to a final tough composite of zirconia-mullite using reaction sintering with CaO has been studied by X-ray diffraction, electron microscopy and microanalysis.