LOW TEMPERATURE INTERNAL FRICTION OF COLD WORKED ZIRCONIUM

E. J. SAVINO1 and E. A. BISOGNI2

1  Departamento de Metalurgia, C. N. E. A., Buenos Aires, Argentina
2  Service de Physique du Solide, C. E. N., Grenoble.


Résumé
Le spectre de frottement interne à basse fréquence du Zirconium de haute pureté a été étudié au moyen d'un pendule de torsion type Kê qui permet d'effectuer des déformations in-situ soit à température ambiante, soit à 78 °K. Après déformation à température ambiante, il apparaît un pic de frottement interne centré à environ 150 °K (à 1 Hz). Après variation de la fréquence de mesure, les valeurs obtenues pour ƊH et τ0 sont respectivement 3 ± 0.4 kcal/mole et 10-5±1 s. Quand les échantillons sont déformés à la température de l'azote liquide et que le frottement interne est mesuré au cours du réchauffement, il apparaît un faible maximum Pí à 130 °K et des pics P21 et P22 à 210-230 °K. Il est aussi détecté une augmentation du frottement interne ainsi qu'un défaut de module à 80 °K. Ces résultats sont analysés en relation avec diverses causes de dissipation d'énergie dans les métaux écrouis.


Abstract
The internal friction spectrum at low frequencies of high purity Zirconium has been studied by means of a conventional Kê type torsion pendulum, which allowed for in situ deformations either at room temperature or 78 °K. After room temperature deformation an internal friction peak P1 centered at about 150 °K (for 1 Hz) was found. Changes of the measuring frequency yields values of ƊH and τ0 of 3 ± 0.4 kcal/mol and l0-5±1 s respectively. When samples were deformed at liquid nitrogen temperature and the internal friction measured during warm-up, it was detected the appearance of a small maximum Pí at 130 °K and peaks P21 and P22 at 210°-230 °K. It was also detected an increase of internal friction and a modulus defect at 80 °K. These result are analysed in terms of possible sources of energy dissipation in cold worked metals.


Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.

Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.

Initial download of the metrics may take a while.