INFLUENCE DE L'IRRADIATION SUR LE PIC DES JOINTS DE GRAINS DE L'ALUMINIUM ET D'UN ALLIAGE ALUMINIUM-LITHIUM

J. WOIRGARD1, J. L. GACOUGNOLLE1, S. SARRAZIN2, J. P. AMIRAULT1, J. de FOUQUET1 and A. SILVENT3

1  Laboratoire de Mécanique et Physique des Matériaux, E. N. S. M. A., rue Guillaume-le-Troubadour, 86, Poitiers
2  Laboratoire de Mécanique et Physique des Matériaux, E. N. S. M. A., rue Guillaume-le-Troubadour, 86, Poitiers, Equipe de Recherche associée au C. N. R. S. n° 123
3  Centre d'Etudes Nucléaires de Grenoble.


Résumé
L'influence de l'irradiation, par neutrons lents, sur la relaxation des joints de grains dans l'aluminium et un alliage d'aluminium lithium a été étudiée par frottement intérieur. Nous avons opéré à basse fréquence en sollicitant en torsion, à faible amplitude, des éprouvettes se présentant sous forme de lamelles. Nous avons admis l'existence d'un spectre gaussien de relaxation et utilisé le formalisme dû à Nowick et Berry. Il a été trouvé que l'irradiation a pour effet : 1) Une diminution du terme d'entropie τ0. 2) Une augmentation de l'énergie d'activation apparente. 3) Une décroissance de l'intensité de relaxation. Nous montrons ensuite que les résultats obtenus peuvent s'interpréter qualitativement au moyen du modèle de Roberts et Barrand. Ce modèle suppose que la relaxation est due au mouvement de réseaux de dislocations situés dans les joints ; ce mouvement étant gêné par la coalescence des défauts d'irradiation au cours du recuit que subit l'éprouvette sur le pendule. L'effet est plus marqué pour l'aluminium-lithium ce qui laisse supposer que l'hélium y contribue de façon notable. Un essai sur le cuivre a montré une influence plus nette de l'irradiation.


Abstract
The effect of irradiation on grain boundary relaxation in Al and an Al-Li alloy has been investigated by internal friction. The specimens, in the form of flat bars, were sollicited in torsion at low frequencies and amplitudes. The existence of a lognormal distribution law was assumed and we used the formalism due to Nowick and Berry. It was found that with increasing irradiation doses : 1) The entropy factor τ0 decreases. 2) The activation energy Hm increases. 3) The relaxation strength Ɗj decreases. Then it will be shown that the results may be interpreted in terms of the model for grain boundary damping in C. F. C. metals proposed by Roberts and Barrand. This model supposes that the relaxation is due to the migration of grain boundary dislocations. The decrease in τ0 may be attributed to pinning of dislocations in some boundaries after segregation of defects due to irradiation and the relaxation strength will decrease with the dislocations migration distance. The defects will also slow down vacancies and, thus, the activation energy will increase. One experiment on irradiated copper showed a very marked effect on the relaxation strength, so it is thought that it will be possible to find similar effets on other C. F. C. metals.


Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.

Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.

Initial download of the metrics may take a while.